Diseño y fabricación de un equipo experimental de desgaste y su prueba con un acero experimental TWIP

Abstract

This work has as main objective the implementation of a computer for wear tests under process "pin on disk" (Pin on Disk). For which the necessary elements of control parameters as rotational speed of the disc, load applied to the specimen, the specimen position on the disc wear and time trial were included. Designed and manufactured equipment was used to measure the wear resistance of a TWIP-20% Mn, Al-2% Si-2% C-0.4% Fe-balance steel. 0.75, 1.19 and 2.05 m / sec, respectively, three different loads on the test pieces, they were 24.5, 44.1 and 68.6 N. For each of these three loads were considered sliding speeds applied.

El presente trabajo tiene como objetivo fundamental la implementación de un equipo para realizar ensayos de desgaste bajo el procedimiento "espiga sobre disco" (Pin on Disk). Para lo cual se incluyeron los elementos necesarios de control de parámetros como velocidad de giro del disco, carga aplicada sobre la probeta, posición de la probeta sobre el disco de desgaste y tiempo del ensayo. El equipo diseñado y fabricado se usó para medir la resistencia al desgaste de un acero TWIP Mn-20%, Al-2%, Si-2%, C-0.4%, Fe-Balance. Se aplicaron tres diferentes cargas sobre las probetas, estas fueron de 24.5, 44.1 y 68.6 N. Para cada una de estas cargas se consideraron tres velocidades de deslizamiento: 0.75, 1.19 y 2.05 m/seg, respectivamente.